PHT-1100 便携式硬度测试仪
|
| Portable Hardness Tester |
| |
|
The PHASE II portable Hardness Tester, Model# PHT-1100 is capable of measuring the surface Hardness and tensile properties of a broad variety of metals on flat and round surfaces. This instrument comes with an integrated Hardness impact probe and digital displaymeter. Users can quickly print test data using the integrated, removable dot matrix printer.
Reliable Hardness property measures of steel and cast steel, alloy steel, gray cast iron, cast iron, cast aluminum alloy, brass, bronze and copper, and tensile property measurements of carbon alloys, steel alloys, ( cr-v, cr-mo, cr-ni-mo, cr-mn-si), super strength alloys and stainless steel alloys are easily attained with this compact instrument.
MEASURING METHOD:
The measuring principle is defined as "the quotient of the impact body’s rebound velocity over its impact velocity". An impact body with a spherical test tip made of tungsten carbide is propelled against the test piece surface by the force of a spring and then rebounds back.
FUNCTIONS PHT-1100
- Display test results in all various Hardness Scales: hrb, hrc, hb, hv, hsd, hl
- Test at any angle, even upside down!
- Conversion to ultimate tensile strength
- Immediate conversion between hardness scales, and print-out if desired
- Input and print-out of test number and date
- Input and print-out of material type and test direction
- Print-out of test results via integral printer
- Low battery indication
- Comes complete with protective carrying case, test block, support ring, cleaning brush and battery charger
|
|
| | |
 |
Technical Specifications
| Overall dimensions |
10.6 x 3.4 x 1.8in. (270 x 86 x 47mm) |
| Total weight |
1.4lb (650g, including impact device and printer) |
| Operating temperature |
Processor: 5-104 degrees Fahrenheit
Impact device: -4 to 248 degrees |
| Measuring accuracy |
+- 0.8% of reading at LD=900 |
| Repeatability |
+- 0.8% of reading at LD=900 |
| Operating voltage |
4.7v – 6.0v (nicd batteries) |
| Hardness measuring ranges |
with standard impact device D |
| HRC 20-68; HRB 13-100; HB 30-650; HV 80-980; HSD 32-100; HL 200-900 |
IMPACT DEVICES: PHASE II MODEL NO. PHT-1100
IMPACT DEVICE D
| Special feature: |
Universal standard unit |
| Application: |
For the majority of hardness testing assignments |
| Weight: |
75g |
IMPACT DEVICE DC
| Special feature: |
Extremely short impact device. Spring loaded with a special loading stick |
| Application: |
Used for very confined spaces (holes, cylinders, or for internal measurements on assembled machines). |
| Weight: |
50g |
IMPACT DEVICE D+15
| Special feature: |
Particularly slim front section and with measuring coil moved back |
| Application: |
Hardness measurements in grooves and on recessed surfaces |
| Weight: |
80g |
IMPACT DEVICE DL
| Special feature: |
Needle front section diameter 2.78mm length=50mm |
| Application: |
Measurements in extremely confined spaces |
| Weight: |
100g |
IMPACT DEVICE C
| Special feature: |
Reduced impact energy (approx. 1/4 of type d) |
| Application: |
Surface hardened components, coatings, thin walled or impact sensitive components (small measuring indentation) |
| Weight: |
75g |
IMPACT DEVICE G
| Special feature: |
Enlarged test tip. (Approx. 9 times larger than type d). Low demands on measuring surface finish. For measurements in the brinel range only (max. 650 hb) |
| Application: |
Solid components such as heavy castings and forging. |
| Weight: |
250g |
IMPACT DEVICE TECHNICAL DATA FOR PHT-1100
| Impact devices |
D/DC/DL |
D+15 |
C |
G |
E |
| Impact energy |
11Nmm |
11Nmm |
3Nmm |
90Nmm |
11Nmm |
| Mass of the impact body |
5. 5g |
7. 8g |
3. 0g |
20g |
5. 5g |
| |
DL: 7.3g |
|
|
|
|
| Test tip |
+- 0.8% of reading at LD=900 |
|
|
|
|
| * Hardness |
1600HV |
1600HV |
1600HV |
1600HV |
5000HV |
| * Diameter |
3mm |
3mm |
3mm |
5mm |
3mm |
| * Material |
|
Tungsten |
Tungsten |
|
Diamond |
| |
|
Carbide |
Carbide |
|
|
| Impact device |
|
|
|
|
|
| * Diameter |
20mm |
20mm |
20mm |
30mm |
20mm |
| * Length |
147/86mm |
162mm |
141mm |
254mm |
155mm |
| * Weight |
75/50g |
80g |
75g |
250g |
80g |
| Max. hardness of sample |
940HV |
940HV |
1000HV |
650HB |
1200HV |
| Preparation of surface |
|
|
|
|
|
| * Roughness class ISO |
N7 |
N7 |
N5 |
N9 |
N7 |
| * Max. roughness depth Rt |
10 µ m |
10 µ m |
2.5 µ m |
30 µ m |
10 µ m |
| * Average roughness Ra |
2 µ m |
2 µ m |
0. 4 µ m |
7 µ m |
2 µ m |
| Min. weight of sample |
|
|
|
|
|
| * Of compact shape |
5kg |
5kg |
1.5kg |
15kg |
5kg |
| * On solid support |
2kg |
2kg |
0.5kg |
5kg |
2kg |
| * Coupled on plate |
0. 1kg |
0. 1kg |
0. 02kg |
0. 5kg |
0. 1kg |
| Min. thickness of sample |
|
|
|
|
|
| * Coupled |
3mm |
3mm |
1mm |
10mm |
3mm |
| * Min. thickness of layers |
0. 8mm |
0. 8mm |
0. 2mm |
- |
0. 8mm |
| Indentation of test tip |
|
|
|
|
|
| With 300 HV |
|
|
|
|
|
| * Diameter |
0. 54mm |
0. 54mm |
0. 38mm |
1.03mm |
0. 54mm |
| * Depth |
24 µ m |
24 µ m |
12 µ m |
53 µ m |
24 µ m |
| with 600 HV |
|
|
|
|
|
| * Diameter |
0. 45mm |
0. 45mm |
0. 32mm |
0. 90mm |
0. 45mm |
| * Depth |
17 µ m |
17 µ m |
8 µ m |
41 µ m |
17 µ m |
| with 800 HV |
|
|
|
|
|
| * Diameter |
0. 35mm |
0. 35mm |
0. 30mm |
- |
0. 35mm |
| * Depth |
10 µ m |
10 µ m |
7 µ m |
- |
10 µ m |
| |
 |
|